Our Product: Stainless Steel Tube & Stainless Steel Semless Pipe, ASTM/AISI 304, 304L, 316, 316L,317,317L,321,310,309S,347,S31803
Chinese Stainless Steel Pipe & Tube & tubing Manufacturer
Random Products
 S31803 Duplex stainless steel seamless pipe
S31803 Duplex stainless steel seamless pipe Alloy  310S TP310S Seamless Stainless Steel pipe
310S TP310S Seamless Stainless Steel pipe  304 Cold Drawn Stainless Steel Seamless Pipe
304 Cold Drawn Stainless Steel Seamless Pipe We ar |
Contact Info
Baofeng Steel Group Co.,Ltd.
Key Contact: Ms. Susan He Tel: 0086-15805786050 Fax: 0086-578-8017518 E-Mail: hesufang1987@hotmail.com    |
TP310S (0Cr25Ni20 , SUS310S ,310S ,310S31 ,1.4845 ,Z8CN25-2) Stainless steel pipe
TIME:2010/11/17/
TP310S (0Cr25Ni20 , SUS310S ,310S ,310S31 ,1.4845 ,Z8CN25-2) Stainless steel pipe
|
0Cr25Ni20 |
-
|
SUS310S
|
310S
|
310S31
|
1.4845
|
Z8CN25-20
|
||
Principal Design Features The strength of this alloy is a combination of good strength and corrosion resistance in temperatures up to 2100 F (1149 C). Due to its relatively high chromium and nickel content it is superior in most environments to 304 or 309 stainless.
Applications Oven linings, boiler baffles, fire box sheets, furnace components and other high temperature containers.
Machinability This alloy machines similarly to type 304 stainless. Its chips are stringy and it will work harden rapidly. It is necessary to keep the tool cutting at all times and use chip breakers.
Welding Most of the austenitic stainless steels can be readily welded using fusion or resistance methods. Oxyacetylene welding is not recommended. Filler metal should be AWS E/ER 310.
Hot Working Most common hot work methods can be successfully performed after uniform heating to 2150 F (1177 C). Do not forge below 1800 F (982 C). Rapid cooling is required to maximize corrosion resistance.
Cold Working Although this alloy has a high work hardening rate, it can be drawn, headed, upset, and stamped. Full annealing is required after cold work to remove internal stress.
Annealing 1900-2050 F (1038-1121 C) water quench.
Hardening This alloy does not respond to heat treatment. Cold work will cause an increase in both hardness and strength.
TP310S (0Cr25Ni20 , SUS310S ,310S ,310S31 ,1.4845 ,Z8CN25-2) Stainless steel pipe
Provious News >> TP309S (0Cr23Ni13 ，SUS309S ) stainless steel pipe
Next News >>TP316 (0Cr17Ni12Mo2 08KH17H13M2T SUS316 316 316S31 1.4401 Z7CND17-12-2 ) stainless steel pipe
About Us |
Company News |
Our Product |
Factory Tour |
Certificate |
Send Inquiry |
Contact Us | Sitemap
Copyright © Baofeng Steel Group Co.,Ltd.. All rights reserved . 浙ICP备10004359号
Copyright © Baofeng Steel Group Co.,Ltd.. All rights reserved . 浙ICP备10004359号
 Chinese |
 English |
 German |
 Spanish |
 French |
 Italian |
 Portuguese |
 Japanese |
 Korean |
 Russian |